High Thermal Resistance grade

UEP

SSP6000

Thermosetting Poly Imides
Stock Shapes [Sintering Process]
~ Natural PI ~

SSP6000 is a typical conventional thermosetting type Poly Imides.

SSP6000’s property and color are similar to a conventional PI.

Features
Heat Resistance:
Tg 410°C / HDT 380°C
Color:
Similar to a conventional PI
ItemsUnitSpecSSP6000Natural PI
Tensile Strength MPa JIS K7161 70 86
Elongation % JIS K7161 4.5 7.5
Flexural Strength MPa JIS K7171 120 110
Flexural Modulus GPa JIS K7171 3.0 3.1
Charpy Impact Strength (Notched) kJ m-2 JIS K7111-1 3.5 -
Surface Resistivity Ω sq-1 ANSI/ESD STM11.13 >1013 >1013
Linear Thermal Expansion (~120°C) ppm °C-1 JIS K7197 - 54
Water Absorption (24hur@23°C) % JIS K7209 0.36 0.24

SCM7000

Natural PBI
Stock Shapes [Compression]

SCM7000 is the compression molded stock shapes by PBI Method using PBI natural grade.

Features
Mechanical property:
High strength and high hardness
High heat resistance:
Super heat resistance, Low thermal expansion and high heat insulation
Plasma resistance:
High plasma durability
Chemical resistance:
High resistance to acid, base, etc, organic solvent
ItemUnitSpecSCM7000
Tensile Strength MPa ASTM D638 160
Elongation % ASTM D638 3.0
Flexural Strength MPa ASTM D790 220
Flexural Modulus GPa ASTM D790 6.5
Izod Impact Strength (Notched) J m-1 ASTM D256 30
Rockwell hardness - ASTM D785 A50
Coefficient of Thermal Expansion ppm °C-1 JIS K7197 23
Heat Deflection Temperature °C ASTM D648 410
Thermal Conductivity W m-1K-1 ASTM F433 0.4
Volume Resistivity Ω m ASTM D257 2.0 x 1013
Specific Gravity - JIS K7112 1.3
Water Absorption % ASTM D570 0.4
Surface Resistivity Ω sq-1 ANSI/ESD STM11.13 >1013

SCM7600

CF reinforced PBI
Stock Shapes [Compression]

SCM7600 is the compression molded stock shapes by PBI Method using carbon fiber reinforced PBI.

Features
Mechanical property:
High-strength and high-hardness
High heat resistance:
Super heat resistance, Low thermal expansion and high heat insulation
Electrical property:
From insulation to conduction - Selectable
Plasma resistance:
High plasma durability
Chemical resistance:
High resistance to acid, base, etc, organic solvent
Tribological property:
Abrasion resistance and low friction coefficient
ItemUnitSpecSCM7600Natural PBI
Tensile Strength MPa ASTM D638 150 160
Elongation % ASTM D638 1.5 3.0
Flexural Strength MPa ASTM D790 245 220
Flexural Modulus GPa ASTM D790 9.5 6.5
Izod Impact Strength (Notched) J m-1 ASTM D256 45 30
Rockwell hardness - ASTM D785 A55 A50
Coefficient of Thermal Expansion ppm °C-1 JIS K7197 28 23
Heat Deflection Temperature °C ASTM D648 410 410
Thermal Conductivity W m-1K-1 ASTM F433 0.4 0.4
Volume Resistivity Ω m JIS K7194 | ASTM D257 1.0 x 10-2 2.0 x 1013
Specific Gravity - JIS K7112 1.3 1.3
Water Absorption % ASTM D570 0.4 0.4
Surface Resistivity Ω sq-1 ANSI/ESD STM11.13 <103 >1013

SCM6000NT1

Polyimide showing
excellent mechanical strength [Compression]
~ PI ~

SCM6000NT1 is made from polyimide provided by Evonik Ind.

Features
Mechanical properties:
Excellent mechanical properties at high temperatures
Heat Resistance:
Tg: 337°C, HDT: 319°C
Storage modulus vs. temperature

ItemUnitSpecSCM6000NT1Standard PI
Tensile Strength MPa JIS K7161 140 86
Elongation % JIS K7161 10 7.5
Flexural Strength MPa JIS K7171 185 110
Flexural Modulus GPa JIS K7171 3.5 3.1
Charpy Impact Strength (Notched) kJ m-2 JIS K7111-1 6 -
Surface Resistivity Ω sq-1 ANSI/ESD STM11.13 >1013 >1013